Evaluation Of Mechanical Properties Of Palm Oil Fuel Ash (pofa) Blended – Granite - Gravel Concrete
-
-
-
3.4 Fresh Concrete Workability
To determine consistency of concrete, Slump test was conducted with uniform water content ratio of 0.5. The workability of the concrete was determine using a cone of 30cm height. The height of subsidence was determined using a ruler.
3.5 Density
To determine the density of the concrete, the weights of the specimens were measured at curing age of 7, 28, 56 and 90 days and using these data the wet and dry density of the samples were determined.
3.6 Determination of Compressive Strength
According to Yi et al. (2006) observation, the impact of cubic and prismatic shape specimens on strength is greater when compared with the cylindrical specimens. In this study, cubes of size 150 mm x 150 mm x 150 mm were cast as per BS EN 12390-3:2009 for testing of compressive strength of specimens. 100% Standard sand compliant to BS EN 12390-3:2009 was used to produce the cubes in 1:2:4 mix ratios. Compressive strength of concrete specimens were measured as per BS EN 12390-3:2009. Immediately after specified curing age, the cubes were placed in compression testing machine in order to test for the compressive strength. The cubes were placed in the machine in such that the load were applied on opposite sides of the cube as cast. The load was applied gently and gradually increased at the rate of 4.5 kN/sec until the resistance of the cube to the increasing load breaks down and no significant load could be sustained after which the highest load applied to the cube were recorded.
-
-
-
ABSRACT - [ Total Page(s): 1 ]ABSTRACTUtilizing Palm Oil Fuel Ash (POFA) in concrete mix is a major way of turning waste to wealth. Gravel as an aggregate is cheaper than granite. Thus, obtaining an optimum combination of these materials in achieving a maximum compressive strength in concrete will go a long way in helping the construction industry.The study was carried out to establish an optimum replacement ratio for Palm Oil Fuel Ash (POFA) blended granite-gravel of concrete. Uniform water/binder (w/b) ratio of 0.5 and mix ... Continue reading---
LIST OF TABLES - [ Total Page(s): 1 ]LIST OF TABLESTable 2. 1: Chemical composition range of OPC and POFA Table 2. 2: Chemical composition analysis in POFA Table 2. 3: Compressive strength of concrete with various percentages of POFA Table 2. 4: Tensile strength of concrete by the addition of various % of POFA Table 3. 1: Concrete mix design based on design expert Table 4. 1: Oxides composition of POFA Table 4. 2: Fine sand grain size distributions from sieve analysis Table 4. 3: Granite size distributions from sieve analysis T ... Continue reading---
LIST OF FIGURES - [ Total Page(s): 1 ]LIST OF FIGURESFigure 2. 1: Strength versus UPV Figure 2. 2: Compressive strength versus POFA replacement percentage Figure 2. 3: Strength activity index of POFA mortar Figure 2. 4: Relationship between UPV and replacement percentage Figure 2. 5: Slump flow against POFA percentage Figure 2. 6: Relationship between porosity and POFA content Figure 2. 7: Relationship between strength and porosity of 80% content of POFA mortar Figure 2. 8: relationship between permeability and replaceme ... Continue reading---
TABLE OF CONTENTS - [ Total Page(s): 1 ]TABLE OF CONTENTSCERTIFICATION DEDICATION ACKNOWLEDGEMENT LIST OF TABLES LIST OF FIGURES ABSTRACT CHAPTER ONE INTRODUCTION 1.1 Background of the study 1.2 Scope 1.4 Justification 1.5 Statement of Problem 1.6 Aim 1.7 Objectives CHAPTER TWO LITERATURE REVIEW 2.1 Properties of concrete with POFA 2.1.1 Physical properties 2.1.2 Chemical Properties of POFA 2.1.3 Mechanical properties of POFA 2.2 Compressive St ... Continue reading---
CHAPTER ONE - [ Total Page(s): 2 ]CHAPTER ONEINTRODUCTION1.1 Background of the study Concrete is regarded as the primary and widely used construction ingredient around the world in which cement is the key material. However, large scale cement production contributes greenhouse gases both directly through the production of CO2 during manufacturing and also through the consumption of energy (combustion of fossil fuels). Moved by the economic and ecological concerns of cement, researchers have focused on finding a subs ... Continue reading---
CHAPTER TWO - [ Total Page(s): 9 ]However, POFA contribute to its long-term strength due to the continuous pozzolanic reaction because of the fine particle size, the greater glassy phase of SiO2 and the reduced composition of carbon (Zeyad et al., 2012). This is also proved by Altwair et al. (2011) using the strength activity index which is the ratio of the strength of SCM-cement mortar to cement mortar at specific curing time. 2.3 Ultrasonic Pulse Velocity (UPV) of Concrete with Replaced POFA According to Kanadasan & ... Continue reading---
CHAPTER FOUR - [ Total Page(s): 15 ]Figure 4.2 shows effect of granite and POFA mix ratio on compressive strength of concrete. The graph shows that, the increase in granite volume led to increase in compressive strength. However, increase in POFA percentage led to decrease in compressive strength. It can be observed that, the highest compressive strength was achieved at 25% POFA replacement and lowest at 35% replacement. Also, for granite highest and lowest compressive strength were achieved at 100% and 0% replacement respectively ... Continue reading---
CHAPTER FIVE - [ Total Page(s): 1 ] CHAPTER FIVECONCLUSION AND RECOMMENDATIONS5.1 Conclusion The study determined the compressive strength of granite-gravel concrete at varying replacement of Palm Oil Fuel Ash (POFA) at different curing ages. Also, established an optimum replacement of Palm Oil Fuel Ash (POFA) blended granite-gravel. Therefore, the following conclusions were drawn:1. The increase in granite volume led to increase in compressive strength. However, increase in POFA percentage led to decrea ... Continue reading---
REFRENCES - [ Total Page(s): 2 ]REFERENCESAltwair, N.M., Johari, M.A.M. and Hashim, S.F.S., 2013. Influence of treated palm oil fuel ash on compressive properties and chloride resistance of engineered cementitious composites. Materials and Structures, 47(4), pp.667–682. Aprianti, E., Shafigh, P., Bahri, S. and Farahani, J.N., (2015). Supplementary cementitious materials origin from agricultural wastes - A review. Construction and Building Materials, 74, pp.176–187. Asrah, H., Mirasa, ... Continue reading---
-
ABSRACT - [ Total Page(s): 1 ]ABSTRACTUtilizing Palm Oil Fuel Ash (POFA) in concrete mix is a major way of turning waste to wealth. Gravel as an aggregate is cheaper than granite. Thus, obtaining an optimum combination of these materials in achieving a maximum compressive strength in concrete will go a long way in helping the construction industry.The study was carried out to establish an optimum replacement ratio for Palm Oil Fuel Ash (POFA) blended granite-gravel of concrete. Uniform water/binder (w/b) ratio of 0.5 and mix ... Continue reading---